H72 SPRINT AIR: Trasparente 2K ad aria ultra rapido - H72 SPRINT AIR: Ultra-fast air-dried 2K clear-coat

1. Trasparente bicomponente Ultra Fast ideale
come finitura di pregio, nei cicli a doppio
strato, ove si utilizzino basi opache ad acqua
o solvente. Ideale per piccole riparazioni
ove siano richiesti tempi di indurimento
particolarmente ridotti.
Ultra Fast two-component clear-coat. Ideal
for high quality finishes, in double layer
cycles wherewater- or solvent-based
mat basecoats are used. Ideal for small
repairs when the product must harden
within a very short time.
H72 SPRINT AIR.
ULTRA-FAST
AIR-DRIED 2K
CLEAR-COAT.
H72 SPRINT AIR.
TRASPARENTE
2K AD ARIA
ULTRA RAPIDO.
www.icrsprint.it

2. IT SCHEDA TECNICA H72
H72 SPRINT AIR
Trasparente 2K ad aria ultra rapido
H72 SPRINT AIR
Ultra-fast air-dried 2K clear-coat
A) DESCRIZIONE E CAMPO D’IMPIEGO:
Trasparente bicomponente Ultra Fast ideale come finitura di pregio, nei
cicli a doppio strato, ove si utilizzino basi opache ad acqua o solvente.
Ideale per piccole riparazioni ove siano richiesti tempi di indurimento
particolarmente ridotti. Le caratteristiche sono la facilità nell’impiego, le
alte rese, l’ottima distensione del film e una rapidità tale da permettere
una lucidabilità già dopo 50-60 min. Il valor massimo di VOC, nella
forma pronta all’uso, in accordo alla Normativa 2004/42, per questo
prodotto appartenenente alla sottocategoria IIB(d) è 340 g/l.
B) NOTE TECNICHE:
Composizione: Resine Speciali di Sintesi
Peso specifico: 1,05 ± 0,03 Kg/Lt
Colori disponibili: Trasparente incolore
Dati di sicurezza: Fare riferimento alla scheda di sicurezza
C) PREPARAZIONE DEL SUPPORTO:
• Base opaca per doppio strato ad acqua e solvente:
per garantire un’ottima adesione tra base opaca e
trasparente è necessario applicare il trasparente
su base opaca catalizzata al 10%
D) AVVERTENZE:
> La reattività del prodotto è influenzata dall’umidità atmosferica,
aumenta all’aumentare dell’umidità.
> Con Umidità inferiore al 40% i tempi di essiccazione sono più lunghi
di quelli indicati
> Utilizzare a Temperature superiori ai 15°C e Umidità Relativa tra
40% e 80%.
E) LAVORAZIONE:
1:1 catalizzatore C72 potlife 20-25 min a 23°C. Preparare la
miscela versando il C72 dentro H72, mai viceversa
Nessuna diluizione, Viscosità 13-15” Ford 4 a 23°C
1,2-1,3 mm 3-4 bar
1/2 + -1 = 45-50 micron
5 minuti
Fuori polvere: 15 minuti a 23°C
Essiccazione completa 50-70 minuti a 23°C
Non applicabile
F) PULIZIA DEGLI ATTREZZI:
> Con diluente per poliuretanici.
Le informazioni tecniche ed i suggerimenti sono conformi a quanto risulta dalle nostre
esperienze. Noi assicuriamo la perfetta qualità del prodotto. Tuttavia, non essendo le
condizioni di utilizzo sotto il nostro controllo, non assumiamo nessuna responsabilità sui
risultati ottenuti.
A) DESCRIPTION AND FIELDS OF APPLICATION:
Ultra Fast two-component clear-coat. Ideal for high quality finishes, in
double layer cycles where water- or solvent-based mat basecoats are
used. Ideal for small repairs when the product must harden within a
very short time. This high-performance product is easy to use, features
excellent spreading capacity and dries so fast that it can be polished
after 50-60 min. In accordance with Standard 2004/42, the maximum
VOC value of this product, which belongs to subcategory IIB(d), is 340
g/l in the ready-to-use form.
B) TECHNICAL DATA:
Composition: Special synthesis resins
Specific weight: 1,05 ± 0,03 Kg/Lt
Available colours: Colourless clear
Safety data: Consult the safety data sheet
C) SURFACE PREPARATION:
• Water- and solvent-based mat basecoat in a double coat:
to ensure that the mat basecoat and clear-coat adhere to each
other in an optimum way, the clear-coat must be applied to the
mat basecoat mixed with 10% hardener
D) CAUTIONS:
> Product reactivity is influenced by atmospheric humidity:
it will increase as humidity rises.
> When humidity is below 40%, drying times are longer than
those indicated.
> Use the product at temperatures above 15°C and at a Relative
Humidity between 40% and 80%.
E) PROCESSING:
1:1 C72 hardener potlife 20-25 min at 23°C. Prepare mixture
by pouring the C72 into the H72, never vice versa
Does not need to be diluted, Viscosity 13-15” Ford 4 at 23°C
1.2-1.3 mm 3-4 bar
1/2 + -1 = 45-50 micron
5 minutes
Dry dust free: 15 minutes at 20°C at 23°C
Completely dry after 50-70 minutes at 23°C
Not applicable
F) TOOLS CLEANING:
> Use thinner for polyurethane products.
Technical indications and advices are based on our own experiences.
We assure the perfect quality of products. However, being the utilization out of our
control, we assume no responsibility on the results obtained.
EN TECHNICAL SHEET H72
INDUSTRIA CHIMICA REGGIANA - I.C.R. S.p.A - Sede e Stabilimento: 42124 Reggio Emilia - Via M. Gasparini, 7 - Tel. +39 0522 517803 - Fax +39 0522 514384
Stabilimento di Lodi: 26817 S. Martino in Strada (LO) - Via del Commercio, 1 - Tel. +39 0371 475313 - Fax +39 0371 475370 - icr@icrsprint.it - www.icrsprint.it
ICR Ibérica S.A. - Pol. Ind. Sta. Magdalena, C/ Guillem Rovirosa 18-24 - 08800 Vilanova i la Geltrú, España - Tel. +34 93 8932695 - Fax +34 93 8143495 - info@icriberica.com