Diese Präsentation wurde erfolgreich gemeldet.
Wir verwenden Ihre LinkedIn Profilangaben und Informationen zu Ihren Aktivitäten, um Anzeigen zu personalisieren und Ihnen relevantere Inhalte anzuzeigen. Sie können Ihre Anzeigeneinstellungen jederzeit ändern.

Silorane composite resin simply discussed 2011

dental Silorane composite resin 2 pages only 2011 simply discussed

  • Als Erste(r) kommentieren

Silorane composite resin simply discussed 2011

  1. 1. * RBC = resin-based composite , RBCs = resin-based composites.Silorane resin-based compositeSilorane resin-based composite ( silorane RBC* ): good biocombatibility and low mutagenic potential( in comparison with oxirane RBC )Note: silorane resin = siloxane & oxirane .Oxirane : Cationic ring opening addition polymerization reaction ( while other methacrylate RBCs arefree radical addition polymerization reaction ).Low polymerization shrinkage ( less than 1% shrinkage, while other composites more than1.5% shrinkage )Less microleakage and better marginal integrity.Less polymerization stress.Siloxane : Increased hydrophobicityLess water sorption ( water sorption may result in hydrolytic degradation andfiller-matrix debonding ).Less absorption to dyes and less sensitive towards exogenic staining( about 50% less than other composites ).Less bacterial adhesion ( about 50% less than other composites ).Less solubility.Initiating system : Combines between ( balance between )High polymerization reactivity ( better than oxirane RBC ).( note: a reactive material develops its strength directly after light cure )Highest ambient light stability ( 10 min , while other composites wereless than 2 min ).( this allows the dentist to place the composite restoration underfull operatory light )Note: The electron donor decomposes the iodonium salt to an acidic cation , which opens the oxirane ring , andstarts the ring opening polymerization reaction.A critical mass of cations has to be formed to start the polymerization reaction. This is the reason for thehighest ambient light stability. ( ambient = surrounding ) , ( ambient light = operatory light )( camphorquinone,iodonium salt,electron donor )
  2. 2. * RBC = resin-based composite , RBCs = resin-based composites.Advantages of silorane RBC :1 , 2 : Low polymerization shrinkage and stress ( less than 1% polymerization shrinkage, while othercomposites more than 1.5% polymerization shrinkage ).3 : Less microleakage and better marginal integrity.4 , 5 : Less water sorption and solubility.6 : Less absorption to dyes and less sensitive towards exogenic staining ( about 50% less than othercomposites ).7 : Less bacterial adhesion ( about 50% less than other composites ).8 : Highest ambient light stability ( 10 min , while other composites were less than 2 min ).Note : Ambient = surrounding.Ambient light = operatory light.( this allows the dentist to place the composite restoration under full operatory light )9 : Good biocombatibility and low mutagenic potential ( in comparison with oxirane RBC ).What is the cause of polymerization shrinkage ?The resin molecules move toward each other to form chemical bond polymerization shrinkage.Why cationic ring-opening addition polymerization reaction resuls in lowerpolymerization shrinkage than free radical addition polymerization reaction ?Because ring opening (opening the ring) gains space and compensate shrinkage which occurs in thesubsequent step ( when the resin molecules move toward each other to form chemical bond ).How can we reduce polymerization stress ?Reducing polymerization shrinkage ( from seminar ), reducing stiffness (elastic modulus),reducing C-factor, incremental placement, curing technique and polymerization speed (e.g soft-startto allow for sress relaxation).

×