2. CASTING DEFECTS
A casting defect is an irregularity in the metal casting process that is undesired.
It can also be defined as conditions in a casting that must be corrected or removed,
or the casting must be rejected.
It may sometimes be tolerated, sometimes eliminated with proper moulding
practice or repaired using methods such as welding, metallization etc.
There are many types of defects which result from many different causes. Some of
the remedies to certain defects may be the cause for another type of defect.
2
3. CASTING DEFECTS
Defects in castings occur due to various causes. Although it is quite difficult to
establish a relationship between defects & causes, casting defects are roughly
broken down into five main categories :
Gas Defects
Shrinkage Cavities
Moulding Material Defects
Pouring Metal Defects
Metallurgical Defects
3
4. CASTING DEFECTS
All of these categories include various types of defects which are shown below:
4
5. MISMATCH or MOULD
SHIFT
The casting that does not match at
the parting line is known as Mismatch
or Mould shift.
Causes :
• Worn out or bent clamping pins.
• Misalignment of two
halves of pattern.
• Improper location &
support of core.
• Faulty core boxes.
• Loose dowels.
5
6. MISMATCH or MOULD
SHIFT
Remedies :
• Increase strength of mould & core.
• Provide adequate support to core.
• Proper alignment of two halves of
the pattern.
• Proper clamping of
mould box.
• Repair or replace dowels
& pin causing mismatch.
6
7. MISRUN & COLD SHUTS
When the metal is unable to fill
the mould cavity completely &
thus leaves unfilled cavities, it is
called as misrun defect.
When two metal streams meeting
in the mould cavity, do not fuse
together properly, causing
discontinuity or weak spot inside
casting, it is called as cold shuts.
7
8. MISRUN & COLD SHUTS
Causes :
• Low pouring temperature.
• Faulty gating system design.
• Too thin casting sections.
• Slow and intermitted pouring.
• Improper alloy composition.
• Use of damaged pattern.
• Lack of fluidity in molten metal.
8
9. MISRUN & COLD SHUTS
Remedies :
• Smooth pouring with the
help of monorail.
• Properly transport mould
during pouring.
• Providing appropriate pouring
temperature.
• Modifying the gating system
design.
9
10. SHRINKAGE CAVITY
Shrinkage cavity is a void on
the surface of the casting
caused mainly due to
uncontrolled and haphazard
solidification of the metal.
Shrinkage defects can be
split into two different types:
1) External shrinkage
2) Closed shrinkage defects.
10
11. SHRINKAGE CAVITY
Causes :
• Inadequate and improper
gating & risering system.
• Too much high pouring
temperature.
• Improper chilling.
Remedies :
• Ensure proper directional
solidification by modifying
gating, risering & chilling
system.
11
12. BLOW HOLES
Balloon shaped gas cavities caused
by release of mould gases during
pouring are known as blow holes.
Causes :
• Ramming is too hard.
• Cores are not sufficiently baked.
• Excess moisture content.
• Low sand permeability.
• Excessive fineness of sand grains.
• Rusted chills, chaplets & inserts.
• Presence of gas producing
ingredients.
12
13. BLOW HOLES
Remedies :
• Baking of cores properly.
• Control of moisture content
in moulding sand.
• Use of rust free chills, chaplets &
inserts.
• Provide adequate venting in
mould and cores.
• Ramming the mould less harder.
13
14. POROSITY
Porosity is in the form of cavities caused due to gas entrapment during
solidification.
Causes :
• High pouring temperature.
• Gas dissolved in metal charge.
• Less flux used.
• Molten metal not properly
degassed.
• Slow solidification of casting.
• High moisture and low
permeability of mould.
14
15. POROSITY
Remedies :
• Regulate pouring temperature
• Control metal composition.
• Increase flux proportions.
• Ensure effective degassing.
• Modify gating and risering.
• Reduce moisture and increase
permeability of mould.
15
16. INCLUSIONS
Any undesirable foreign particle present within the metal of a casting is called as
inclusions.
It may be oxides, sand, slag, dirt etc., which enters the mould cavity with the molten
metal during pouring & weakens the casting & also spoils the surface of the casting.
Causes :
• Faulty gating & pouring.
• Dissolved gases in molten metal.
• Inferior molding or core sand.
• Soft ramming of mold.
• Rough handling of mold and core.
16
SAND INCLUSION
17. INCLUSIONS
Remedies :
• Modify gating system.
• Improve pouring to minimize turbulence.
• Use of superior sand of good strength.
• Provide hard ramming.
• Use slag trapping methods for
preventing any slag from entering
the mould cavity.
17
SAND INCLUSION
18. HOT TEARS or
HOT CRACKING
Hot tears are ragged irregular
internal or external cracks
occurring immediately after the
metal have solidified.
Causes :
• Lack of collapsibility of
core & mould.
• Hard ramming of mould.
• Faulty casting design.
Remedies :
• Providing softer ramming.
• Improve casting design.
• Improve collapsibility of core
& mould.
18
19. METAL PENETRATION
Penetration occurs when the
molten metal flows between the
sand particles in the mould.
Causes :
• Low strength of moulding sand.
• Large size of moulding sand.
• High permeability of sand.
• Soft ramming.
Remedies :
• Use of fine grain with low
permeability.
• Appropriate ramming.
19
20. PIN HOLES
Formation of many small gas cavities
at or slightly below surface of casting
is called as pin holes.
Causes :
• Sand with high moisture content.
• Absorption of hydrogen/carbon
monoxide gas in the metal.
• Alloy not being properly degassed.
• Sand containing gas producing ingredients.
Remedies :
• Reducing the moisture content & increasing permeability of moulding sand.
• Employing good melting and fluxing practices.
• Improving a rapid rate of solidification.
20
21. SWELL
A swell is an enlargement of mould
cavity by localized metal pressure.
Causes :
• Insufficient or soft ramming.
• Low strength mould & core.
• Mould not being supported
properly.
Remedies :
• Sand should be rammed evenly and properly.
• Increase strength of mould & core.
21
22. DROP
Drop is a projection on drag part of
casting due fall of its cope part.
Causes :
• Low green strength of the moulding
sand.
• Low mould hardness.
• Insufficient reinforcement of sand projections in the cope.
Remedies :
• Moulding sand should have sufficient green strength.
• Provide adequate reinforcement to sand projections and cope by using nails and
gaggers.
• Ramming should not be too soft.
22
23. FLASHES or FINS
A thin projection of metal not
intended in casting, usually
occurring at parting line is
called as fins.
Causes :
• Inadequately weighted sand
• Over flexible bottom boards.
• Defective moulding box.
• Loose plates and improper clamping of flasks.
Remedies :
• Correct assembly of the mould and cores.
• Keep weights on mold boxes.
• Change the defective moulding box.
23
24. RAT TAILS or BUCKLES
Slight compression failure of a thin layer
of moulding sand is called as rat tails &
more severe compression failure is called
as buckles i.e. Buckling of sand.
Causes :
• Excessive mould hardness.
• Lack of combustible additives in the moulding sand.
• Continuous large surfaces on the casting.
Remedies :
• Suitable addition of combustible additives to moulding sand.
• Reduction in mould hardness.
• Modifications in casting design.
24
25. WARPAGE
Warpage is an undesirable deformation in a casting occurring during or after
solidification due to improper solidification.
Causes :
• Continuous large flat surfaces.
• No directional solidification of casting.
• Moulding sand having too low green strength.
• Improper cooling rate.
Remedies :
• Follow principle of sufficient directional solidification.
• Make good casting & gating system design.
• Proper selection of moulding sand.
25
26. CRACKED CASTING
These are cracks caused by inability of
casting to cope with internal stresses
resulting from solid shrinkage of metal
Immediately after solidification some
metals have low strength and if stresses
set up are high cracks developed in the
casting.
Cracks can be avoided by proper
design of casting, avoiding joining of
unequal stresses ,providing round
corners etc
26
27. BENT OR TWISTED
CASTING
When a casting has wide variation in
its sections, internal stresses are always
set up in it due to differential cooling in
thick n thin areas. This leads to casting
warpage.
The remedy is to provide suitable
allowances in pattern, controlling
deformation by performing suitable
ribs and plan for uniform cooling rate
27
28. OPEN BLOWS AND BLOW
HOLES
Open blows are smooth cavities or voids on
the surface of the casting .blow holes are
bubbles of gas entrapped inside the casting
.both are caused by gases carried by hot
metals.
Blow holes are also caused by poor
permeability of sand, too fine sand grains,
over rammed moulds or insufficient venting.
Blow holes can be controlled by controlling
moisture content, providing proper venting
,not too hard ramming of the mould and
controlling binder content
28
29. FUSION
When mould sand has not enough
refractoriness or metal is poured at very high
temperature or facing sand is of poor quality,
the sand melts and fuse with the casting
surface.
This makes difficult to clean castings and
gives them rough glossy appearance
Using sand of enough refractoriness and
pouring at suitable temp can eliminate this
defect
29
30. RUNOUT
A run out occurs when molten metal
leaks out of the mould during
pouring . This is caused by defecting
moulding boxes , faulty clamping
and weighing and by casting too near
the edge of the box
Run out is avoided by modifying the
moulding system , providing proper
parting line and providing proper
gating system.
30
31. CRACK
Cracks may arise from locked up stresses set
up by non uniform heating and cooling
,excess sulphur or phosphorus in the metal,
and some other causes.
31